MgO (Magnesium Oxide)

Magnesium Oxide can be used for high temperature windows and substrates. HTSC substrates.

Physical and optical properties 

Transmission Range :	0.3 to 6 μm
Refractive Index :	1.7085 at 2 μm (1)
Reflection Loss :	12.8% at 2 μm (2 surfaces)
Absorption Coefficient :	0.05 cm-1 at 5.5 μm
Reststrahlen Peak :	n/a
dn/dT :	+19 x 10-6 /°C
dn/dμ = 0 :	n/a
Density :	3.58 g/cc
Melting Point :	2800 °C
Thermal Conductivity :	42 W m-1 K-1 at 273K
Thermal Expansion :	10.8 x 10-6 /°C at 273K
Hardness :	Knoop 692 with 600g indenter
Specific Heat Capacity :	877 J Kg-1 K-1
Dielectric Constant :	9.65 at 1 MHz
Youngs Modulus (E) :	249 GPa
Shear Modulus (G) :	155 GPa
Bulk Modulus (K) :	155 GPa
Elastic Coefficients :	C11=294; C12=93; C44=155
Apparent Elastic Limit :	138 MPA (20,000 psi)
Poisson Ratio :	0.18
Solubility :	0.00062g/100g Water
Molecular Weight :	40.32
Class/Structure :	Cubic FCC, NaCl, Fm3m, (100) cleavage

 

 

 

Refractive Index  

 

No = Ordinary Ray

µm	No	µm	No	µm	No
0.171	2.319	0.180	2.138	0.191	2.039
0.200	1.986	0.230	1.892	0.276	1.824
0.310	1.795	0.382	1.7668	0.436	1.75471
0.50	1.754	0.644	1.734	1.00	1.7229
2.00	1.7085	3.00	1.6915	4.00	1.6679
5.00	1.6373	6.02	1.5957	7.04	1.543
8.07	1.475	9.09	1.389	10.64	1.209

 

 

Product Notes

Magnesium Oxide is grown in relatively small sizes, mainly in Japan and China.

Tags: MgO (Magnesium Oxide)

---